Estándares AA Grado 5050 O
Propiedades
Generales
| Propiedad | Valor | Condición | Estándares relacionados |
|---|---|---|---|
| Densidad | 2,69 g/cm³ | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Mecánica
| Propiedad | Valor | Condición | Estándares relacionados | Comentario |
|---|---|---|---|---|
| Resistencia a la fatiga por flexión | 85,0 MPa | O | Normas AA | |
| Módulo elástico | 69,0 GPa | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
| Dureza, Brinell | 36.0 [-] | O | Normas AA | |
| Tenacidad a la fractura por deformación plana | 22,0 - 35,0 MPa·√m | Típico para aluminio forjado serie 5000 | ||
| Relación de Poisson | 0.33 [-] | Típico para aluminio forjado serie 5000 | ||
| Módulo de corte | 26,0 - 26,5 GPa | Típico para aluminio forjado serie 5000 | ||
| Resistencia a la tracción | 125,0 - 165,0 MPa | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | |
| 125,0 MPa | O | Normas AA, ASTM B483 | ||
| 145,0 MPa | O | Normas AA |
térmica
| Propiedad | Temperatura | Valor | Condición | Estándares relacionados | Comentario |
|---|---|---|---|---|---|
| Coeficiente de dilatación térmica | 20 °C | 2.38e-05 1/K | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
| 100 °C | 2.38e-05 1/K | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
| Temperatura máxima de servicio | 150,0 °C | Típico para aluminio forjado serie 5000 | |||
| Punto de fusión | 625,0 - 650,0 °C | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
| Capacidad calorífica específica | 879,0 - 963,0 J/(kg·K) | Típico para aluminio forjado serie 5000 | |||
| Conductividad térmica | 193 W/(m·K) | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Eléctrico
| Propiedad | Valor | Condición | Estándares relacionados |
|---|---|---|---|
| Conductividad eléctrica | 29000000.0 S/m | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
| Resistividad eléctrica | 3,45e-08 Ω·m | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Propiedades químicas
| Propiedad | Valor | Condición | Estándares relacionados |
|---|---|---|---|
| Cromo | 0,1 % | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
| Cobre | 0,2 % | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
| Hierro | 0,70 % | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
| Magnesio | 1,1 - 1,8 % | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
| Manganeso | 0,1 % | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
| Silicio | 0,4 % | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
| Cinc | 0,25 % | O | Normas AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Propiedades tecnológicas
| Propiedad | ||
|---|---|---|
| Brazing | general:Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen
| |
| Propiedades de corrosión | Agrietamiento por corrosión bajo tensión:sin daño durante la operación y pruebas de laboratorio, general:muy bueno, sin protección en atmósfera industrial o de agua de mar
| |
| Mecanizabilidad general | General:no apto (O), pobre (H32, H34), suficiente (H36, H38)
| |
| Trabajabilidad | general (estado):bueno (O, H32), aceptable (H34), malo (H36, H38)
| |
Metal
- ASTM B483 Grado 5050 O
- ASTM B210 Grado 5050 O
- Estándares AA Grado 5050 H22
- Estándares AA Grado 5050 H26
- Estándares AA Grado 5050 H24
- Estándares AA Grado 5456 O
- Estándares AA Grado 5050 H112
- Estándares AA Grado 5083 O
- Estándares AA Grado 6066 T6
- Estándares AA Grado 6351 T6
- Estándares AA Grado 5050 H34